| About |
|---|
| RONFALIN® C C130 U是一种聚碳酸酯+丙烯腈丁二烯苯乙烯(PC+ABS)材料,。 该产品在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货,。 RONFALIN® C C130 U的主要特性有: 阻燃/额定火焰 良好的抗紫外线能力 紫外线稳定 RONFALIN® C C130 U的典型应用领域为:房屋&& |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 15 | g/10min | ISO 1133 |
| Shrinkage rate | 0.50 to 0.70 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2400 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 55.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | > 50 | % | ISO 527-2 |
| Bending modulus | 2300 | MPa | ISO 178 |
| bending strength | 80.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 45.0 | kJ/m² | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 125 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 108 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 130 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |