| About |
|---|
| RONFALIN® HX10 U is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Important attributes of RONFALIN® HX10 U are: Flame Rated RoHS Compliant Heat Resistant Typical application of RONFALIN® HX10 U: Automotive&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Material Status | Commercial: Active |
| Features | High Heat Resistance,Weather resistance is good |
| Availabilitys | Asia Pacific,North America,Latin America,Africa & Middle East ,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 4.0 | g/10min | ISO 1133 |
| Shrinkage rate | 0.40 to 0.60 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 12 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 107 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 105 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 110 | ℃ | ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+16 | ohms | IEC 60093 |
| Dielectric strength | > 25 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | |||
| Solution A | > 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 | |
| Burning rate | |||
| 2.0 mm | < 100 | mm/min | FMVSS 302 |
| 2.0 mm | < 100 | mm/min | ISO 3795 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | 98.0 | MPa | ISO 2039-1 |
| tensile strength | |||
| yield | 48.0 | MPa | ISO 527-2/50 |
| Bending modulus | 2500 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |