| About |
|---|
| Standard SAN grade for injection molding and extrusion. This grade is available with and without UV stabilization.&& |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | SAN |
| Material Status | Commercial: Active |
| Features | Weather resistance is good |
| Availabilitys | Africa & Middle East ,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.08 | g/cm³ | ISO 1183/A |
| Melt Volume Rate | |||
| 230℃，3.8 kg | 5.00 | cm³/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 17 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 102 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed | 98.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| A50 | 110 | ℃ | ISO 306/A50 |
| B50 | 101 | ℃ | ISO 306 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 165 | MPa | ISO 2039-1 |
| Tensile modulus | 3700 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| fracture | 70.0 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 3.0 | % | ISO 527-2/1A/5 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 180 to 200 | °C | |
| Barrel middle temperature | 210 to 230 | °C | |
| Barrel front temperature | 240 to 250 | °C | |
| Nozzle temperature | 240 to 260 | °C | |
| Processing (melt) temperature | 220 to 250 | °C | |
| Mold temperature | 50 to 80 | °C | |
| Injection pressure | 100 to 150 | MPa | |
| Injection speed | 中等偏快 | ||
| Hold pressure | 30.0 to 90.0 | MPa | |
| Back pressure | 5.00 to 15.0 | MPa | |
| Screw Speed | < 36 | m/min | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |