| About |
|---|
| 35% glass fiber reinforced SAN compound&& |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | SAN |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability |
| Availabilitys | Africa & Middle East ,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.35 | g/cm³ | ISO 1183/A |
| Melt Volume Rate | |||
| 220℃，10 kg | 5.00 | cm³/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 3.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 9.0 | kJ/m² | ISO 179/1eU |
| 23℃ | 15 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 101 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed | 98.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| A50 | 112 | ℃ | ISO 306/A50 |
| B50 | 105 | ℃ | ISO 306 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 77.0 | MPa | ISO 2039-1 |
| Tensile modulus | 12500 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| fracture | 96.0 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 1.0 | % | ISO 527-2/1A/5 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |