| Rotec® ABS 1001 TR-AC是一种丙烯腈丁二烯苯乙烯(ABS)材料,。 该产品在欧洲有供货,加工方式为:挤出或注射成型。 Rotec® ABS 1001 TR-AC的主要特性为:阻燃/额定火焰。&& |
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.11 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 17 | g/10min | ISO 1133 |
| Shrinkage rate | 0.30 to 0.70 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 0.30 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 2400 | MPa | ISO 527-1-2 |
| tensile strength | |||
| Yield, 23 ℃ | 50.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Fracture, 23 ℃ | 15 | % | ISO 527-2/50 |
| Bending modulus | |||
| 23℃ | 2600 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 60.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 80 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 84.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 93.0 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | < 80.0 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.050 | % | |
| Proposed maximum recycled material ratio | 5 | % | |
| Barrel rear temperature | 210 to 250 | °C | |
| Barrel middle temperature | 210 to 250 | °C | |
| Barrel front temperature | 210 to 250 | °C | |
| Processing (melt) temperature | < 260 | °C | |
| Mold temperature | 40.0 to 80.0 | °C | |
| Drying temperature | < 80.0 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.050 | % | |
| Barrel 1 zone temperature | 190 to 210 | °C | |
| Barrel 2 zone temperature | 190 to 210 | °C | |
| Barrel 3 zone temperature | 190 to 210 | °C | |
| Barrel 4 zone temperature | 190 to 210 | °C | |
| Barrel 5 zone temperature | 190 to 210 | °C | |
| Melt temperature | < 245 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |