| About |
|---|
| ROTOUN® PP350P is a Polypropylene product. It can be processed by rotational molding and is available in Asia Pacific. Typical application: Tanks. Characteristics include: Flame Rated RoHS Compliant Good Mold Release Heat Stabilizer Mold Release Agent&& |
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Good stripping performance,Heat Stabilized |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.901 | g/cm³ | ISO 1183 |
| Apparent density | 0.35 | g/cm³ | ISO 60 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 10 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | 1000 | hr | ASTM D1693 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod notched impact strength | 60.0 | J/cm | ARM |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 81.0 | ℃ | ISO 75-2/B |
| Embrittlement temperature | -40.0 | ℃ | ISO 974 |
| Vicat Softening Temp | 130 | ℃ | ISO 306 |
| Melting temperature | 164 | ℃ | ISO 11357-3 |
| Oxygen sensing time | 50 | min | ISO 11357 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+17 | ohms | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| UV Rating | 2000 | hr | ASTM D2565 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 66 | ISO 868 | |
| tensile strength | |||
| yield | 20.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 25 | % | ISO 527-2 |
| Bending modulus | 1050 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |