| ESD Protection – Electrically Conductive – Extrusion Grade |
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Conductive,Electrostatic discharge protection |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | < 1.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 4480 | MPa | ASTM D638 |
| Tensile strength | 29.0 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 2.0 to 4.0 | % | ASTM D638 |
| Bending modulus | 4140 | MPa | ASTM D790 |
| bending strength | 49.6 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 53 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 3.2 mm | 210 | J/m | ASTM D4812 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | < 1.0E+3 | ohms | ASTM D257 |
| Volume resistivity | < 1.0 | ohms·cm | ASTM D257 |
| Process Conditions | |||
|---|---|---|---|
| extrusion | Nominal value | Unit | Test method |
| drying temperature | 79 | °C | |
| Drying time | 2.0 | hr | |
| Melt Temperature | 191 to 232 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |