| About |
|---|
| Glass Fiber – Flame Retardant – UV Stabilized&& |
| Product Description | |
|---|---|
| Generic | PA6 |
| Material Status | Commercial: Negative |
| Features | Weather resistance is good,Flame Characteristics,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.80 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.080 to 0.20 | % | ASTM D955 |
| water content | 0.20 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 18600 | MPa | ASTM D638 |
| tensile strength | 193 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 2.0 | % | ASTM D638 |
| Bending modulus | 17900 | MPa | ASTM D790 |
| bending strength | 310 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 140 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 3.2 mm | 960 | J/m | ASTM D4812 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 204 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Primary Additive | 50 | % |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 2.0 | hr | |
| Dew Point | -18 | °C | |
| Processing (melt) temperature | 243 to 279 | °C | |
| Mold temperature | 54 to 93 | °C | |
| Injection pressure | 68.9 to 103 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |