Product Description
GenericPolyetherimide
Material StatusCommercial: Negative
FeaturesGood liquidity,Lubricating,V-0
AvailabilitysAfrica & Middle East ,North America,Latin America,Asia Pacific,Europe
Process MethodsInjection Molding

Technical Data
PHYSICALNominal valueUnitTest method
Density1.35g/cm³ASTM D792
Shrinkage rate
MD:3.2 mm0.80%ASTM D955
Water absorption rate
23℃,24hr0.25%ASTM D570

IMPACTNominal valueUnitTest method
Impact strength of cantilever beam notch
3.2mm48J/mASTM D256
Notched impact strength of cantilever beam
3.2 mm430J/mASTM D4812

THERMALNominal valueUnitTest method
Hot deformation temperature ASTM D648
0.45 MPa, unannealed207ASTM D648
1.8 MPa, unannealed196ASTM D648
Linear coefficient of thermal expansion
MD5.6E-51/℃ASTM D696
Thermal conductivity coefficient0.22W/m/KASTM C177

Electrical performanceNominal valueUnitTest method
Volume resistivity1.0E+16ohms·cmASTM D257
Dielectric strength20kV/mmASTM D149
Dielectric constant
1 MHz3.20 ASTM D150
Dissipation factor
1 MHz4.0E-3 ASTM D150

FLAME CHARACTERISTICSNominal valueUnitTest method
Flame retardant levelV-0 UL 94

MECHANICALNominal valueUnitTest method
Rockwell hardness
R-level118 ASTM D785
Tensile modulus3100MPaASTM D638
tensile strength82.7MPaASTM D638
Tensile strain
fracture8.0%ASTM D638
Bending modulus2900MPaASTM D790
bending strength114MPaASTM D790
compressive strength110MPaASTM D695
friction coefficient
&Metal – Dynamic0.15 ASTM D1894

Process Conditions
injectionNominal valueUnitTest method
Drying temperature149°C
Drying time4.0hr
Recommended maximum moisture content0.020%
Proposed maximum recycled material ratio20%
Barrel rear temperature343 to 399°C
Barrel middle temperature343 to 399°C
Barrel front temperature343 to 399°C
Mold temperature93 to 177°C
Injection pressure103 to 138MPa
Back pressure0.345 to 0.517MPa
Clamping force6.9 to 11kN/cm²

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.