| Warning: The status of this material is ‘Commercial: Limited Issue’ The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. RTP 2580 C HEC FR Series materials are polycarbonates/ABS alloys with nickel-coated carbon fiber added for electrical conductivity and EMI/RFI shielding. These materials meet the flammability requirements of UL94 V-0 and are available in a range of colors.&& |
| Product Description | |
|---|---|
| Generic | PC+ABS |
| Material Status | Commercial: Negative |
| Features | Conductive,Flame Characteristics,EMI,RFI,Antistatic property,V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.20 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.10 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 7580 | MPa | ASTM D638 |
| tensile strength | 89.6 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1.5 | % | ASTM D638 |
| Bending modulus | 6210 | MPa | ASTM D790 |
| bending strength | 131 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 53 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 3.2 mm | 270 | J/m | ASTM D4812 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 110 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+5 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+3 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.6 mm，RTP Tested | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 99 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Proposed maximum recycled material ratio | 20 | % | |
| Barrel rear temperature | 232 to 288 | °C | |
| Barrel middle temperature | 232 to 288 | °C | |
| Barrel front temperature | 232 to 288 | °C | |
| Mold temperature | 71 to 99 | °C | |
| Injection pressure | 68.9 to 103 | MPa | |
| Back pressure | 0.345 | MPa | |
| Clamping force | 6.9 to 11 | kN/cm² | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |