| Product Description | |
|---|---|
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Negative |
| Features | Excellent Processability,Conductive,Electrostatic discharge protection,Solvent resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.80 to 1.2 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.050 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 无断裂 | ASTM D256 | |
| Notched impact strength of cantilever beam | |||
| 3.2 mm | 无断裂 | ASTM D4812 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -30.0 | ℃ | ASTM D746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+6 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+3 | ohms·cm | ASTM D257 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 90 | ASTM D2240 | |
| Tensile modulus | 276 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 9.65 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 300 | % | ASTM D638 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 177 to 232 | °C | |
| Barrel middle temperature | 177 to 232 | °C | |
| Barrel front temperature | 177 to 232 | °C | |
| Mold temperature | 16 to 66 | °C | |
| Injection pressure | 68.9 to 138 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |