| P-60 is a high durometer, high modulus, platinum-catalyzed, RTV-2 silicone rubber designed for casting polyurethanes and epoxies. It is easy to mix and de-air, and will cure with virtually no shrinkage. The speed at which the rubber hardens can be dramatically accelerated with heat or with Pt Accelerator at room temperature. Addition-cure two-component siliconerubbers may show inhibition sensitivity. P-60 offers outstanding chemical and heat resistance and the rigidity to withstand the expansion of most polyurethane foams.&& |
| Product Description | |
|---|---|
| Generic | 硅橡胶,RTV-2 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low contractility,High Heat Resistance,Solvent resistance |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 | g/cm³ | |
| Thermosetting mixed viscosity | Nominal value | Unit | Test method |
|---|
| Uncured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| colour | |||
| — | Blue | ||
| — | Tan | ||
| viscosity | |||
| — | 1.0 to 2.0 | Pa·s | |
| — | 130 to 160 | Pa·s | |
| Curing time | 16 to 24 | hr | |
| storage stability | 60 to 120 | min |
| Cured Properties | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 54 to 62 | ||
| Shaw’s A | 58 to 66 | ||
| tensile strength | 5.58 to 6.83 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 180 to 230 | % | ASTM D412 |
| tear strength | 11.4 to 14.9 | kN/m | ASTM D624 |
| Coverage（Cured） | 0.809 | cm³/g |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Operating temperature | |||
| Cured | -51 to 343 | ℃ | |
| Thermosetting components | |||
| resin | 按容量计算的混合比: 100 按重量计算的混合比: 10 | ||
| Hardening method | 按容量计算的混合比: 14 按重量计算的混合比: 1.0 | ||
| Storage period | 26 | wk |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Mixed |
| 3. Activator |
| 4. Base |
| 5. 1 Day |
| 6. 7 Days |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |