| Product Description | |
|---|---|
| Supplier | DuPont |
| Material Status | Commercial: Negative |
| Features | Flame Characteristics,V-0 |
| Availabilitys | Africa & Middle East ,Latin America,Europe,Asia Pacific,North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | |||
| 150℃ | 5050 | MPa | ASTM D638 |
| 93℃ | 8210 | MPa | ASTM D638 |
| 23℃ | 16500 | MPa | ASTM D638 |
| -40℃ | 17100 | MPa | ASTM D638 |
| 23℃ | 17000 | MPa | ISO 527 |
| tensile strength | |||
| 150℃ | 55.2 | MPa | ASTM D638 |
| 93℃ | 86.5 | MPa | ASTM D638 |
| 23℃ | 172 | MPa | ASTM D638 |
| -40℃ | 210 | MPa | ASTM D638 |
| 23℃ | 170 | MPa | ISO 527 |
| elongation | |||
| 150℃ | 5.5 | % | ASTM D638 |
| 93℃ | 4.3 | % | ASTM D638 |
| 23℃ | 1.8 | % | ASTM D638 |
| -40℃ | 1.7 | % | ASTM D638 |
| 23℃ | 1.8 | % | ISO 527 |
| Tensile creep modulus | |||
| 1000 hr | 15000 | MPa | |
| bending strength | |||
| 150°C | 79.3 | MPa | ASTM D790 |
| 93°C | 138 | MPa | ASTM D790 |
| 23°C | 248 | MPa | ASTM D790 |
| 23°C | 310 | MPa | ASTM D790 |
| Bending modulus | |||
| 150°C | 29000 | MPa | ASTM D790 |
| 93°C | 68900 | MPa | ASTM D790 |
| 23°C | 14500 | MPa | ASTM D790 |
| -40℃ | 15200 | MPa | ASTM D790 |
| 150°C | 31000 | MPa | ISO 178 |
| 93°C | 68900 | MPa | ISO 178 |
| 23°C | 14500 | MPa | ISO 178 |
| shear strength | |||
| 23°C | 58.6 | MPa | ASTM D732 |
| compressive strength | |||
| 23°C | 231 | MPa | ASTM D695 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 96 | J/m | ASTM D256 |
| -30℃ | 91 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 750 | J/m | ASTM D256 |
| -30℃ | 510 | J/m | ASTM D256 |
| Charpy Notched Impact Strength | |||
| 23℃ | 10 | kJ/m² | ISO 179 |
| -30℃ | 10 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 43 | kJ/m² | ISO 179 |
| -30℃ | 30 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 247 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 224 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 240 | ℃ | ISO 75 |
| 1.8 MPa, unannealed | 225 | ℃ | ISO 75 |
| Melting temperature | 254 | ℃ | ISO 11357 |
| Linear coefficient of thermal expansion | |||
| TD | 5E-4 | cm/cm/℃ | ASTM D696 |
| MD | 7.9E-5 | cm/cm/℃ | ASTM D696 |
| TD | |||
| -40 to 23 ℃ | 5E-4 | cm/cm/℃ | ASTM E228 |
| MD | |||
| -40 to 23 ℃ | 5.5E-5 | cm/cm/℃ | ASTM E228 |
| TD | 5E-4 | cm/cm/℃ | ISO 11359 |
| MD | 7.9E-5 | cm/cm/℃ | ISO 11359 |
| TD | |||
| -40 to 23 ℃ | 5E-4 | cm/cm/℃ | ISO 11359 |
| MD | |||
| -40 to 23 ℃ | 5.5E-5 | cm/cm/℃ | ISO 11359 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 1.0E+14 | ohms·cm | ASTM D257 | |
| 1.0E+14 | ohms·cm | IEC 60093 | |
| Surface resistivity | |||
| 1.0E+13 | ohm | ASTM D257 | |
| 1.0E+13 | ohm | IEC 60093 | |
| Insulation strength | |||
| 95°C 1.6mm | 21.5 | kV/mm | ASTM D149 |
| 23°C 1.6mm | 23.5 | kV/mm | ASTM D149 |
| 32 | kV/mm | IEC 60243 | |
| Dielectric constant | |||
| 1 MHz | 4.1 | ASTM D150 | |
| 1 KHz | 4.1 | ASTM D150 | |
| 1 MHz | 4.1 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 0.017 | ASTM D150 | |
| 1 KHz | 0.009 | ASTM D150 | |
| 1 MHz | 0.017 | IEC 60250 | |
| Compared to the leakage tracing index | |||
| 250 | V | IEC 60112 | |
| 2 | PLC | IEC 60112 | |
| High voltage arc marking rate (HVTR) | 1 | PLC | UL 746A |
| High Arc Burning Index (HAI) | |||
| Natural black 0.81 mm | 1 | PLC | UL 746A |
| Natural black 1.5 mm | 1 | PLC | UL 746A |
| Natural black 3.0 mm | 1 | PLC | UL 746A |
| Arc resistance | 5 | PLC | ASTM D495 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| Natural black 0.81 mm | V-0 | UL 94 | |
| Natural black 1.5 mm | V-0 5VA | UL 94 | |
| Natural black 3.0 mm | V-0 5VA | UL 94 | |
| Extreme oxygen index | |||
| 35 | % | ASTM D2863 | |
| 35 | % | ISO 4589 | |
| Relative Heat Index, Elec | |||
| Natural black 0.81 mm | 155 | ℃ | UL 746B |
| Natural black 1.5 mm | 155 | ℃ | UL 746B |
| Natural black 3.0 mm | 155 | ℃ | UL 746B |
| Relative heat index, lmp | |||
| Natural black 0.81 mm | 155 | ℃ | UL 746B |
| Natural black 1.5 mm | 155 | ℃ | UL 746B |
| Natural black 3.0 mm | 155 | ℃ | UL 746B |
| Relative heat index, Str | |||
| Natural black 0.81 mm | 155 | ℃ | UL 746B |
| Natural black 1.5 mm | 155 | ℃ | UL 746B |
| Natural black 3.0 mm | 155 | ℃ | UL 746B |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.79 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.13 | % | ASTM D955 |
| MD | 0.48 | % | ASTM D955 |
| TD | 0.2 | % | ISO 294 |
| MD | 0.75 | % | ISO 294 |
| Water absorption rate | |||
| 50% RH | 0.11 | % | ISO 62 |
| 50% RH | 0.62 | % | ISO 62 |
| Ash Content | 43 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |