| Ryton® XE5515BL 15% glass fiber reinforced polyphenylene sulfide alloy compound provides excellent mechanical strength and chemical resistance at elevated temperatures and is suitable for extrusion or blow molding.&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Solvent resistance,V-0 |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.42 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 316℃，5.0kg | 12 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 | % | |
| TD：3.2 mm | 0.60 | % | |
| Water absorption rate | |||
| 23℃，24hr | 0.010 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm | 96 | J/m | ASTM D256 |
| — | 10 | kJ/m² | ISO 180-A |
| Notched impact strength of cantilever beam | |||
| 3.2 mm | 690 | J/m | ASTM D4812 |
| — | 45 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 190 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | ASTM E831 | ||
| MD：-50~50℃ | 3.0E-5 | 1/℃ | ASTM E831 |
| MD：100~200℃ | 2.0E-5 | 1/℃ | ASTM E831 |
| TD：-50~50℃ | 5.5E-5 | 1/℃ | ASTM E831 |
| TD：100~200℃ | 9.0E-5 | 1/℃ | ASTM E831 |
| Thermal conductivity coefficient | 0.23 | W/m/K |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | 24 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 25 ℃，1 kHz | 3.60 | ASTM D150 | |
| 25 ℃，1 MHz | 3.50 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 25℃，1 kHz | 2.0E-3 | ASTM D150 | |
| 25℃，1 MHz | 5.0E-3 | ASTM D150 | |
| Arc resistance | 100 | sec | ASTM D495 |
| Compared to the leakage tracing index | 150 | V | UL 746 |
| insulation resistance | |||
| 90℃ | 1.0E+13 | ohms |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.6 mm，Tested by CP Chemical | V-0 | UL 94 | |
| Extreme oxygen index | 50 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | ||
| M-level | 118 | ASTM D785 | |
| R-level | 87 | ASTM D785 | |
| Tensile modulus | |||
| — | 6210 | MPa | ASTM D638 |
| — | 5800 | MPa | ISO 527-2 |
| tensile strength | |||
| — | 103 | MPa | ASTM D638 |
| — | 110 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.9 | % | ASTM D638 , ISO 527-2 |
| Bending modulus | |||
| — | 5520 | MPa | ASTM D790 |
| — | 5500 | MPa | ISO 178 |
| bending strength | |||
| — | 159 | MPa | ASTM D790 |
| — | 170 | MPa | ISO 178 |
| Poisson’s ratio | 0.41 | ISO 527 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 95%RH, 48 hr |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |