| S.O.E.™ is a new hydrogenated styrenic elastomer based on Asahi’s advanced polymerization and hydrogenation technologies, that open the way to new concepts, developments, and solutions in plastic products. Its unique characteristics have brought fast-rising demand in rapidly expanding applications.&& |
| Product Description | |
|---|---|
| Supplier | Asahi Kasei |
| Generic | SBC |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good Clarity,Good flexibility,Low density,Good wear resistance,High scratch resistance |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.988 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 2.6 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shaw’s A | 80 | ISO 868 | |
| Shore A, 10 seconds | 67 | ISO 868 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ISO 37 | ||
| yield | 12.0 | MPa | ISO 37 |
| 100% strain | 5.10 | MPa | ISO 37 |
| 200% strain | 6.90 | MPa | ISO 37 |
| 300% strain | 8.00 | MPa | ISO 37 |
| Tensile strain | |||
| fracture | 480 | % | ISO 37 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Dunlop Rebound Resilience（23℃） | 12 | % | BS 903 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type 3, 20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |