| About |
|---|
| SABIC®COHERE™8108L是通过使用茂金属催化剂的溶液聚合制备的乙烯 – 辛烯共聚物。 它 在高性能LLDPE吹膜应用中表现良好，具有优异的韧性，热粘性，密封性 和光学性质。 它含有滑脱和防粘剂添加剂。 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | POP |
| Material Status | Commercial: Active |
| Features | Good Hermeticity |
| Availabilitys | Africa & Middle East ,North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| performance | Nominal value | Unit | Test method |
| Polymer properties | Nominal value | Unit | Test method |
|---|
| Density | Nominal value | Unit | Test method |
|---|
| Melt Flow Rate | Nominal value | Unit | Test method |
|---|---|---|---|
| 190℃，2.16kg | 0.8 | g/10 min | ASTM D1238 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Slippery agent | – | – | SABIC method |
| Anti caking agent | – | – | SABIC method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | 6 | % | ASTM D1003 |
| Tensile test film | Nominal value | Unit | Test method |
|---|---|---|---|
| Pressure breakthrough | |||
| TD | 54 | MPa | ASTM D882 |
| MD | 45 | MPa | ASTM D882 |
| Tensile strain | |||
| TD | 640 | % | ASTM D882 |
| MD, fracture | 540 | % | ASTM D882 |
| 1% secant modulus (MD) | 95 | MPa | ASTM D882 |
| 1% secant modulus (MD) | 105 | MPa | ASTM D882 |
| Drop hammer impact | |||
| F50 | > 1000 | g | ASTM D1709 |
| tear strength | Nominal value | Unit | Test method |
|---|---|---|---|
| MD | 13 | g/µm | ASTM D1922 |
| tm | 20 | g/µm | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| melting point | ~105 | ℃ | SABIC method |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |