| CYCOLOY C2951 is a flame retardant PC+ABS free from chlorinated or brominated flame retardant additives. High heat resistance is offered for demandingelectrical applications, whilst maintaining excellent processability. It is listed under UL-94 5VA at 3.0 mm |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | 64 | MPa | ASTM D 638 |
| Tensile strain | 80 | % | ASTM D638 |
| Tensile modulus | 2893.95 | MPa | ASTM D638 |
| bending strength | 92.214 | MPa | ASTM D790 |
| Bending modulus | 2550.6 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 59 | kg.cm/cm | ASTM 2565 |
| Instrument impact total energy | |||
| 23℃ | 550 | cm-kgf | ASTM D 3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 105 | ℃ | ASTM D1525 |
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 6.4 mm | 94 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 89 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 6.4 mm | 103 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 7.2E-05 | 1/℃ | ASTM E831 |
| MD：-40~40℃ | 7.2E-05 | 1/℃ | ASTM E831 |
| Relative temperature index | 85.0 | ℃ | UL 746B |
| Impact mechanical performance | 85.0 | ℃ | UL 746B |
| Flame retardant level | |||
| 1.49 mm | V-0 | UL 94 | |
| 2.48 mm | 5VB | UL 94 | |
| 2.99 mm | 5VA | UL 94 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.19 | ASTM D792 | |
| Dissolution rate | |||
| 3.2 mm | 0.4 – 0.6 | % | SABIC Method |
| 260℃ / 2.16 kgf | 10 | g/10 min | ASTM D 1238 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |