| About |
|---|
| POE C1070 is an ethylene octene copolymer produced by solution polymerization using metallocene catalyst. This product is available as free flowing pellets. |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Negative |
| Features | High liquidity,Low density |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.868 | ASTM D792 | |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| 230℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| Mooney viscosity | |||
| ML 1+4，121℃ | MU | ASTM D1646 | |
| elastic body | Nominal value | Unit | Test method |
|---|
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting peak temperature | 62 | °C | SABIC method |
| Glass transition temperature | -52 | °C | SABIC method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 1 second | 71 | ASTM D1238 | |
| Shore D, 1 second | 21 | ASTM D1238 | |
| Bending modulus | |||
| 1% tangent | 13.2 | ASTM D790 A | |
| tear strength | |||
| C-type | 39.2 | ASTM D624 | |
| tensile property | |||
| Fracture stress | 9.3 | MPa | ASTM D638 |
| Tensile strain | 850 | % | ASTM D638 |
| 100% modulus | 2.9 | MPa | ASTM D638 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |