SABIC® HDPE B6246LS

About
SABIC® HDPE B6246LS is typically used in food and beverage packaging, offering good purity and organoleptics as well as recycle ability. It combines a high rigidity with very good processing performance, which offers potential for system cost reduction. The grade is typically used for the blow moulding of mono as well as multi layer bottles in several food markets, like fresh, pasteurised and ultra heat treated milk, sauces, orange juice, functional drinks, probiotics and other “daily shot” drinks. The material properties offer the possibility to reduce weight at good top load strength. This slip agent free grade is also typically used for the injection moulding of caps & closures for carbonated soft drinks and sparkling water as well as high environmental stress crack resistant applications, like UN-pails and UN-caps & closures. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

About

SABIC® HDPE B6246LS is typically used in food and beverage packaging, offering good purity and organoleptics as well as recycle ability. It combines a high rigidity with very good processing performance, which offers potential for system cost reduction. The grade is typically used for the blow moulding of mono as well as multi layer bottles in several food markets, like fresh, pasteurised and ultra heat treated milk, sauces, orange juice, functional drinks, probiotics and other “daily shot” drinks. The material properties offer the possibility to reduce weight at good top load strength. This slip agent free grade is also typically used for the injection moulding of caps & closures for carbonated soft drinks and sparkling water as well as high environmental stress crack resistant applications, like UN-pails and UN-caps & closures. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

Product Description
Supplier	SABIC
Generic	HDPE
Material Status	Commercial: Active
Features	Good Rigidity,Excellent Processability,High purity,Renewable resources,Food contact compliance,Good sensory characteristics.,High density,High ESCR
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.962	g/cm³	ISO 1183
Melt Flow Rate			ISO 1133
190℃，2.16kg	0.50	g/10min
190℃，21.6kg	46	g/10min
190℃，5.0kg	2.5	g/10min
ESCR(Environmental Stress Cracking Resistance)
10% non-ionic detergent, molded, F50	15.0	hr	ASTM D1693B

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch			ISO 180/A
-30 ℃, molded	7.0	kJ/m²
23 ℃, molded	13	kJ/m²

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	89.0	℃	ISO 75-2/B
Vicat Softening Temp	129	℃	ISO 306/A
Melting temperature
DSC	135	℃	ISO 11357-3
Enthalpy Change	225	J/g	ISO 11357-3

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D, molded	64		ISO 868
Tensile modulus
2 mm, molded into shape	1300	MPa	ISO 527-2/1BA/50
tensile strength			ISO 527-2/1BA/50
Yield, 2 mm, molded	29.0	MPa
Fracture, 2 mm, molded	18.0	MPa
Tensile strain
Fracture, 2 mm, molded	> 1000	%	ISO 527-2/1BA/50
Bending modulus
2 mm, molded into shape	1600	MPa	ISO 178
bending strength
2 mm, molded into shape	31.0	MPa	ISO 178

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.