| About |
|---|
| BM1052是一种具有宽分子量分布的高分子量高密度聚乙烯共聚物牌号。 它有 优异的加工性能和极高的抗冲击强度，刚度和卓越的抗环境应力开裂性能。BM1052树脂适用于吹塑大型容器，如封闭式集装箱，油箱和汽车工业用容器。 它也可以被挤压成具有特别高冲击强度的片材。 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,High ESCR |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.05 | g/10min | ASTM D1238 |
| 190℃，5.0kg | 0.38 | g/10min | ASTM D1238 |
| 190℃，21.6kg | 10 | g/10min | ASTM D1238 |
| Density | 0.952 | g/cm³ | ASTM D1505 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 63 | ASTM D2240 | |
| 1% secant modulus | 1000 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 27 | MPa | ASTM D638 |
| fracture | 18 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | >500 | % | ASTM D638 |
| bending strength | 26 | MPa | ASTM D790 |
| Bending modulus | 1050 | MPa | ISO 178/1A |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 100% non-ionic detergent, F50 | >1200 | hr | ASTM D1693B |
| 10% non-ionic detergent, F50 | 720 | hr | ASTM D1693B |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 125 | ℃ | ASTM D1525 |
| Brittle temperature | <-75 | ℃ | ASTM D746 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod notched impact strength | 300 | J/m | ASTM D256 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |