SABIC® HDPE CC3054

About
SABIC® HDPE CC3054 is a high density polyethylene copolymer injection moulding grade. Its narrow molecular weight distribution and high flow results in low warpage, good rigidity, good gloss and fast moulding cycles. SABIC® HDPE CC3054 is typically used for caps and closures applications and thin wall articles. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

About

SABIC® HDPE CC3054 is a high density polyethylene copolymer injection moulding grade. Its narrow molecular weight distribution and high flow results in low warpage, good rigidity, good gloss and fast moulding cycles. SABIC® HDPE CC3054 is typically used for caps and closures applications and thin wall articles. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

Product Description
Supplier	SABIC
Generic	HDPE copolymer
Material Status	Commercial: Active
Features	Low warping,High liquidity,Quick molding cycle,Weight distribution,Copolymer,High density
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.954	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	30	g/10min	ISO 1133
ESCR(Environmental Stress Cracking Resistance)
60 ℃, 3.00 mm, detergent	40.0	hr	Internal Method

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23 ℃, molded	3.0	kJ/m²	ISO 180-A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	82.0	℃	ISO 75-2/B
Vicat Softening Temp	125	℃	ISO 306/A
Melting temperature
DSC	132	℃	ISO 11357-3
Enthalpy Change	205	J/g	ISO 11357-3

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D, molded	61		ISO 868
Tensile modulus
2 mm, molded into shape	1100	MPa	ISO 527-2/1BA/50
tensile strength			ISO 527-2/1BA/50
Yield, 2 mm, molded	26.0	MPa
Fracture, 2 mm, molded	25.0	MPa
Tensile strain
Fracture, 2 mm, molded	> 200	%	ISO 527-2/1BA/50
Bending modulus
2 mm, molded into shape	1250	MPa	ISO 178
bending strength
2 mm, molded into shape	27.0	MPa	ISO 178

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.