| About |
|---|
| SABIC® HDPE F00950 resin is a high molecular weight, high density polyethylene copolymer. The design of the product, molecular architecture and density, gives F00950 a good balance of easy extrusion and high melt strength with strong physical properties. SABIC® HDPE F00950 is typically used for production of thin films with good strength and rigidity. The material contains anti-oxidants. Typical applications SABIC® HDPE F00950 resin is typically used for blown film extrusion and production of high strength grocery sacks, shopping bags and high quality thin films for multi wall sack liners and replacement for thin paper products. This product is not intended for and must not be used in any pharmaceutical/medical applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | HMW-HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Inoxidizability,High molecular weight,Good melt strength,Copolymer,High density |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.950 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，2.16kg | 0.070 | g/10min | ISO 1133 |
| 190℃，21.6kg | 8.5 | g/10min | ISO 1133 |
| 190℃，5.0kg | 0.30 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Tensile modulus | ISO 527-3 | ||
| MD, 25 µ m, blow molded film | 620 | MPa | ISO 527-3 |
| TD, 25 µ m, blow molded film | 620 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, yield, 25 µ m, blow molded film | 30.0 | MPa | ISO 527-3 |
| TD, yield, 25 µ m, blow molded film | 30.0 | MPa | ISO 527-3 |
| MD, fracture, 25 µ m, blow molded film | 40.0 | MPa | ISO 527-3 |
| TD, fracture, 25 µ m, blow molded film | 50.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 25 µ m, blow molded film | > 300 | % | ISO 527-3 |
| TD, fracture, 25 µ m, blow molded film | > 400 | % | ISO 527-3 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod notched impact strength | |||
| 25 µ m, blow molded | 350 | J/cm | ASTM D4272 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | ISO 6383-2 | ||
| MD，25 µm | 6.0 | kN/m | ISO 6383-2 |
| TD，25 µm | 20.0 | kN/m | ISO 6383-2 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 200 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Blown Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |