| About |
|---|
| SABIC® HDPE F04660 is a homopolymer film grade with a broad processing window and high stiffness. It has good moisture barrier properties and can be blended with LDPE and LLDPE to improve film strength and rigidity. SABIC® HDPE F04660 is a high density polyethylene blow moulding grade for high rigidity, good toughness and processability. These properties offer bottles to be made at lower weight with good top load strength. Typical applications Blown Film: SABIC® HDPE F04660 is typically used for applications where high stiffness is required. It can be used in the middle layer in a coex structure or blended with LDPE and LLDPE to increase stiffness and mechanical properties. It has good water vapor barrier properties required for certain food packaging. Blow Moulding: SABIC® HDPE F04660 can be used in hollow thinwalled parts and profile extrusions. It is not recommended for packaging environmentally active materials such as soaps, detergents, shampoos, etc. This product is not intended for and must not be used in any pharmaceutical/medical applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good flexibility,Moisture resistance,High density,Homopolymer |
| Availabilitys | Europe |
| Process Methods | Profile extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.961 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.70 | g/10min | ASTM D1238 |
| 190℃，21.6kg | 46 | g/10min | ASTM D1238 |
| 190℃，5.0kg | 3.0 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 10% non-ionic detergent, molded, F50 | 15.0 | hr | ASTM D1693B |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Elastic modulus | |||
| TD, 25 µ m, blow molded film | 1700 | MPa | ASTM D882 |
| MD, 25 µ m, blow molded film | 1250 | MPa | ASTM D882 |
| Tensile strain | |||
| Fracture, 2 mm, molded | > 1000 | % | ISO 527-2/1BA/50 |
| MD, fracture, 25 µ m, blow molded film | 490 | % | |
| TD, fracture, 25 µ m, blow molded film | 3.0 | % | |
| Drop hammer impact | |||
| 25 µ m, blow molded film | < 20 | g | ASTM D1709 |
| Elmandorf tear strength | |||
| MD: 25 µ m, blow molded film | 10 | g | |
| TD: 25 µ m, blow molded film | 800 | g |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -30 ℃, molded | 6.0 | kJ/m² | |
| 23 ℃, molded | 10 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 88.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 129 | ℃ | ASTM D1525 |
| Melting temperature | 134 | ℃ | ISO 11357-3 |
| Enthalpy Change | 223 | J/g | ISO 11357-3 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Blow molding barrel temperature | 175 to 200 | ℃ | |
| Blow Molding Melt Temperature | 205 | ℃ | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 63 | ISO 868 | |
| Tensile modulus | |||
| 2 mm, molded into shape | 1250 | MPa | ISO 527-2/1BA/50 |
| tensile strength | |||
| Yield, 2 mm, molded | 29.0 | MPa | |
| Fracture, 2 mm, molded | 18.0 | MPa | |
| Bending modulus | |||
| 2 mm, molded into shape | 1550 | MPa | ISO 178 |
| bending strength | |||
| 2 mm, molded into shape | 31.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 190 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. F50 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |