| About |
|---|
| SABIC® HDPE F0863 resin is a homopolymer with a very high density manufactured by gas phase technology. The grade offers high stiffness, high temperature resistance, low water vapour transmission and a very low gel level. Because of the linear character it is advisable to use the material in combination with extrusion coating LDPE grades like SABIC® LDPE 2005EC in order to improve extrusion coating processability (motorload and Neck In). Application SABIC® HDPE F0863 is typically used for food packaging, release paper and photographic paper. This product is not intended for and must not be used in any pharmaceutical/medical applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low speed solidification point,High Heat Resistance,Inoxidizability,High density,Homopolymer |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.964 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 8.0 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Tensile modulus | ISO 527-3 | ||
| MD, 25 µ m, cast thin film | 580 | MPa | |
| TD, 25 µ m, cast thin film | 580 | MPa | |
| tensile strength | ISO 527-3 | ||
| MD, yield, 25 µ m, blow molded film | 26.0 | MPa | |
| TD, yield, 25 µ m, blow molded film | 24.0 | MPa | |
| MD, fracture, 25 µ m, blow molded film | 22.0 | MPa | |
| TD, fracture, 25 µ m, blow molded film | 18.0 | MPa | |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 25 µ m, cast thin film | 700 | % | |
| TD, fracture, 25 µ m, cast thin film | 800 | % | |
| Oxygen permeability | |||
| 23 ℃, 25 µ m, cast thin film | 0.100 | cm³/m²/24 hr | Internal Method |
| Water vapor transmittance | |||
| 38 ℃, 100% RH, 25 µ m, cast thin film | 4.0 | g/m²/24 hr | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 130 | ℃ | ISO 306/A |
| Melting temperature | |||
| DSC | 134 | ℃ | DIN 53765 |
| Enthalpy Change | 224 | J/g | DIN 53765 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Shrinkage 1 | 168.0 | mm | |
| Minimum coating weight 2 | 2.0 | g/m² | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Measured on pilot line at 400 m/min, 300°C, airgap 300 mm |
| 3. Measured on pilot line at 200 m/min, 300°C, 10 g/m², airgap 300 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |