| About |
|---|
| SABIC® HDPE FI0750 is a high molecular high density polyethylene copolymer grade typically used for blown film applications. SABIC® HDPE FI0750 features are balance between toughness and stiffness, good impact properties with low gel level. Typical applications SABIC® HDPE FI0750 is typically used for blown film extrusion. Typical applications are heavy duty bags, grocery sacks, shopping bags, refuse bags, liners for multi-wall sacks and liners for frozen food meat. The grade can be blended with LLDPE and LDPE and can be used in co-extrusion process. This product is not intended for and must not be used in any pharmaceutical/medical applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | HMW-HDPE |
| Material Status | Commercial: Active |
| Features | High impact resistance,Low speed solidification point,High molecular weight,Copolymer,High density |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.950 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，21.6kg | 7.5 | g/10min | ISO 1133 |
| 190℃，5.0kg | 0.22 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 61 | ISO 868 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 20 | µm | |
| tensile strength | ISO 527-3 | ||
| MD, yield, 20 µ m, blow molded film | 50.0 | MPa | ISO 527-3 |
| TD, yield, 20 µ m, blow molded film | 45.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 20 µ m, blow molded film | 400 | % | ISO 527-3 |
| TD, fracture, 20 µ m, blow molded film | 450 | % | ISO 527-3 |
| Drop hammer impact | |||
| 20 µ m, blow molded film | 250 | g | ASTM D1709 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -80.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 74.0 | ℃ | ISO 306/B |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | ISO 6383-2 | ||
| MD，20 µm | 200.0 | kN/m | ISO 6383-2 |
| TD，20 µm | 425.0 | kN/m | ISO 6383-2 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 200 to 225 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. F50 |
| 3. Blown Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |