SABIC® HDPE FI1157

About
SABIC® HDPE FI1157 is a high molecular high density polyethylene copolymer grade typically used for blown film applications. Its high molecular weight, broad molecular weight distribution and high density enables convertors to produce film with low gels level, high stiffness, impact resistance and with narrow gauge tolerances at low film thickness. SABIC® HDPE FI1157 can be processed at high throughput with good bubble stability. Typical applications SABIC® HDPE FI1157 is typically used for the production of inliners, bitumen release foils, lamination and paper lamination films, labels, artificial paper, thin films for bag on roll and heavy duty bags. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications.&&

About

SABIC® HDPE FI1157 is a high molecular high density polyethylene copolymer grade typically used for blown film applications. Its high molecular weight, broad molecular weight distribution and high density enables convertors to produce film with low gels level, high stiffness, impact resistance and with narrow gauge tolerances at low film thickness. SABIC® HDPE FI1157 can be processed at high throughput with good bubble stability. Typical applications SABIC® HDPE FI1157 is typically used for the production of inliners, bitumen release foils, lamination and paper lamination films, labels, artificial paper, thin films for bag on roll and heavy duty bags. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications.&&

Product Description
Supplier	SABIC
Generic	HMW-HDPE
Material Status	Commercial: Active
Features	Good Rigidity,High impact resistance,Wide molecular weight distribution,Low speed solidification point,High molecular weight,Copolymer,High density
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.957	g/cm³	ISO 1183/A
Melt Flow Rate			ISO 1133
190℃，21.6kg	11	g/10min
190℃，5.0kg	0.35	g/10min

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	62		ISO 868

film	Nominal value	Unit	Test method
film thickness
test	20	µm
tensile strength			ISO 527-3
MD, yield, 20 µ m	50.0	MPa
TD, yield, 20 µ m	45.0	MPa
Tensile strain			ISO 527-3
MD, fracture, 20 µ m	400	%
TD, fracture, 20 µ m	450	%
Drop hammer impact
20 µm	240	g	ASTM D1709

THERMAL	Nominal value	Unit	Test method
Embrittlement temperature	< -80.0	℃	ASTM D746
Vicat Softening Temp	75.0	℃	ISO 306/B

Supplementary information	Nominal value	Unit	Test method
tear strength			ISO 6383-2
MD，20 µm	200.0	kN/m
TD，20 µm	450.0	kN/m

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	200 to 225	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.