SABIC® HDPE ICP4907S

About
SABIC® HDPE ICP4907S is part of SABIC’s high density polyethylene Industrial Container Product portfolio. SABIC® HDPE ICP4907S is typically used for state of the art blow moulding UN certified Intermediate Bulk Containers and Heating Oil Tanks, up to 1000 liters and more. This UV-stabilised and food approved grade combines good processing performance with good stress crack resistance, stiffness and impact performance. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

About

SABIC® HDPE ICP4907S is part of SABIC’s high density polyethylene Industrial Container Product portfolio. SABIC® HDPE ICP4907S is typically used for state of the art blow moulding UN certified Intermediate Bulk Containers and Heating Oil Tanks, up to 1000 liters and more. This UV-stabilised and food approved grade combines good processing performance with good stress crack resistance, stiffness and impact performance. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

Product Description
Supplier	SABIC
Generic	HDPE
Material Status	Commercial: Active
Features	Food contact compliance,Excellent Processability,Good Rigidity,High density,Weather resistance is good,High impact resistance,Good tear strength
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.949	g/cm³	ISO 1183
Melt Flow Rate
190℃，21.6kg	7.0	g/10min	ISO 1133

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
-30 ℃, molded	17	kJ/m²	ISO 180-A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	77.0	℃	ISO 75-2/B
Vicat Softening Temp	126	℃	ISO 306/A
Melting temperature
DSC	131	℃	ISO 11357-3
Enthalpy Change	192	J/g	ISO 11357-3

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D, molded	60		ISO 868
Tensile modulus
2 mm, molded into shape	950	MPa	ISO 527-2/1BA/50
tensile strength			ISO 527-2/1BA/50
Yield, 2 mm, molded	23.0	MPa
Fracture, 2 mm, molded	34.0	MPa
Tensile strain
Fracture, 2 mm, molded	> 1000	%	ISO 527-2/1BA/50
Bending modulus
2 mm, molded into shape	1000	MPa	ISO 178
bending strength
2 mm, molded into shape	24.0	MPa	ISO 178
ESCR(Environmental Stress Cracking Resistance)
Strain Hardening – Gp	30.0	MPa	Internal Method

	Nominal value	Unit	Test method

	Nominal value	Unit	Test method

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.