| About |
|---|
| SABIC® HDPE M40053S SABIC® HDPE M40053S is typically used for the high demanding dustbin market. It is an UV stabilized HDPE copolymer grade. It typically shows a good combination of processability, consistency and product properties, good stiffness/cold impact-balance, surface quality and weatherability properties. Typical applications. SABIC® HDPE M40053S is typically used for the manufacture of injection molded dustbins (waste containers on wheels and household containers), crates & boxes (pallet boxes, pallets, boxes applied at low temperatures) and pails & container applications (industrial, shipping). This product is not intended for and must not be used in any pharmaceutical/medical applications.&&SABIC® HDPE M40053S M40053S is UV stabilized High Density Polyethylene grade with narrow molecular weight distribution suitable for injection molding applications. It has been designed to provide good balance of stiffness and impact at low temperatures and is also having good weatherability and surface properties. M40053S is specially developed for high demanding dust bin market, shipping containers for low temperature storage, industrial pails etc.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | HDPE copolymer |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Excellent Processability,Good surface appearance,Food contact compliance,Weight distribution,Copolymer,High density,low-temperature impact resistance |
| Availabilitys | North America,Latin America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.953 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，2.16kg | 4.0 | g/10min | ISO 1133 |
| 190℃，5.0kg | 11 | g/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, molded | 4.0 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 81.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 124 | ℃ | ISO 306/A |
| Melting temperature | |||
| DSC | 132 | ℃ | ISO 11357-3 |
| Enthalpy Change | 203 | J/g | ISO 11357-3 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 61 | ISO 868 | |
| Tensile modulus | |||
| 2 mm, molded into shape | 1050 | MPa | ISO 527-2/1BA/50 |
| tensile strength | ISO 527-2/1BA/50 | ||
| Yield, 2 mm, molded | 26.0 | MPa | ISO 527-2/1BA/50 |
| Fracture, 2 mm, molded | 25.0 | MPa | ISO 527-2/1BA/50 |
| Tensile strain | |||
| Fracture, 2 mm, molded | > 200 | % | ISO 527-2/1BA/50 |
| Bending modulus | |||
| 2 mm, molded into shape | 1200 | MPa | ISO 178 |
| bending strength | |||
| 2 mm, molded into shape | 26.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 232 to 260 | °C | |
| Mold temperature | 20 to 40 | °C | |
| Injection pressure | 93.0 to 103 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |