SABIC® HDPE M40060S

About
SABIC® HDPE M40060S is an UV stabilized, high density polyethylene copolymer injection moulding grade with a narrow molecular weight distribution. It has improved mouldability. Articles produced from this grade typically show good impact strength, low warpage, stress crack resistance (ESCR) and good gloss. Typical applications. SABIC® HDPE M40060S is typically used for the manufacture of injection moulded articles such as pails, shipping containers and industrial parts. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

About

SABIC® HDPE M40060S is an UV stabilized, high density polyethylene copolymer injection moulding grade with a narrow molecular weight distribution. It has improved mouldability. Articles produced from this grade typically show good impact strength, low warpage, stress crack resistance (ESCR) and good gloss. Typical applications. SABIC® HDPE M40060S is typically used for the manufacture of injection moulded articles such as pails, shipping containers and industrial parts. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

Product Description
Supplier	SABIC
Generic	HDPE copolymer
Material Status	Commercial: Active
Features	Weather resistance is good,Low warping,High impact resistance,Weight distribution,Copolymer,High density,High ESCR
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.960	g/cm³	ISO 1183
Melt Flow Rate			ISO 1133
190℃，2.16kg	4.0	g/10min
190℃，5.0kg	11	g/10min
ESCR(Environmental Stress Cracking Resistance)
60 ℃, 3.00 mm, detergent, molded	70.0	hr	Internal Method

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23 ℃, molded	5.0	kJ/m²	ISO 180-A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	90.0	℃	ISO 75-2/B
Vicat Softening Temp	127	℃	ISO 306/A
Melting temperature
DSC	133	℃	ISO 11357-3
Enthalpy Change	219	J/g	ISO 11357-3

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D, molded	64		ISO 868
Tensile modulus
2 mm, molded into shape	1300	MPa	ISO 527-2/1BA/50
tensile strength			ISO 527-2/1BA/50
Yield, 2 mm, molded	30.0	MPa
Fracture, 2 mm, molded	24.0	MPa
Tensile strain
Fracture, 2 mm, molded	> 200	%	ISO 527-2/1BA/50
Bending modulus
2 mm, molded into shape	1500	MPa	ISO 178
bending strength
2 mm, molded into shape	30.0	MPa	ISO 178

Process Conditions
injection	Nominal value	Unit	Test method
Processing (melt) temperature	232 to 260	°C
Mold temperature	20.0 to 40.0	°C
Injection pressure	93.0 to 103	MPa

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.