| SABIC® HDPE M453SE is typically used for the high demanding dustbin market. It is an UV stabilized HDPE copolymer grade. It typically shows a good combination of processability, consistency and product properties, good stiffness/cold impact-balance, surface quality and weatherability properties. Typical applications. SABIC® HDPE M453SE is typically used for the manufacture of injection molded dustbins (waste containers on wheels and household containers), crates & boxes (pallet boxes, pallets, boxes applied at low temperatures) and pails & container applications (industrial, shipping). This product is not intended for and must not be used in any pharmaceutical/medical applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | HDPE copolymer |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Copolymer,low-temperature impact resistance,Weather resistance is good,Good surface appearance,High density,Excellent Processability |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.953 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，2.16kg | 4.0 | g/10min | |
| 190℃，5.0kg | 11 | g/10min | |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 60 ℃, 3.00 mm, detergent, molded | 65.0 | hr | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact strength | |||
| 23 ℃, molded | 5.0 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 0.45 MPa, unannealed | 81.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temperature | 124 | ℃ | ISO 306/A |
| Melting temperature | |||
| DSC | 132 | ℃ | ISO 11357-3 |
| Enthalpy Change | 203 | J/g | ISO 11357-3 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 61 | ISO 868 | |
| Tensile Modulus | |||
| 2 mm, molded into shape | 1100 | MPa | ISO 527-2/1BA/50 |
| Tensile Strength | ISO 527-2/1BA/50 | ||
| Yield yld, 2 mm, molded | 26.0 | MPa | |
| Broken BRK, 2 mm, molded | 31.0 | MPa | |
| Tensile Strain | |||
| Broken BRK, 2 mm, molded | > 200 | % | ISO 527-2/1BA/50 |
| Flexural Modulus | |||
| 2 mm, molded into shape | 1200 | MPa | ISO 178 |
| Flexural Strength | |||
| 2 mm, molded into shape | 26.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Melt Temperature | 232 to 260 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C | |
| Injection pressure | 93.0 to 103 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |