SABIC® HDPE M864E

About
SABIC® HDPE M864E is a high density polyethylene injection moulding grade with a narrow molecular weight distribution. It is typically used for injection moulding applications where rigidity, toughness and warp resistance are required. SABIC® HDPE M864E is available with UV stabilizer as SABIC® HDPE M864SE and M864SG. Typical applications. Crates & Boxes: SABIC® HDPE M864E is typically used for the manufacture of injection moulded cases, crates, trays, industrial pails and other similar items. Caps & Closures: SABIC HDPE® M864E is typically used for Juice, Milk and Edible Oil applications. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

About

SABIC® HDPE M864E is a high density polyethylene injection moulding grade with a narrow molecular weight distribution. It is typically used for injection moulding applications where rigidity, toughness and warp resistance are required. SABIC® HDPE M864E is available with UV stabilizer as SABIC® HDPE M864SE and M864SG. Typical applications. Crates & Boxes: SABIC® HDPE M864E is typically used for the manufacture of injection moulded cases, crates, trays, industrial pails and other similar items. Caps & Closures: SABIC HDPE® M864E is typically used for Juice, Milk and Edible Oil applications. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

Product Description
Supplier	SABIC
Generic	HDPE
Material Status	Commercial: Active
Features	Weather resistance is good,Good flexibility,High elastic,Weight distribution,High density
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.964	g/cm³	ISO 1183
Melt Flow Rate			ISO 1133
190℃，2.16kg	8.0	g/10min	ISO 1133
190℃，5.0kg	22	g/10min	ISO 1133
ESCR(Environmental Stress Cracking Resistance)
40 ℃, 1.00 mm, 10% wetting agent, molded	7.00	hr	Internal Method

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23 ℃, molded	4.0	kJ/m²	ISO 180-A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	94.0	℃	ISO 75-2/B
Vicat Softening Temp	129	℃	ISO 306/A
Melting temperature
DSC	134	℃	ISO 11357-3
Enthalpy Change	226	J/g	ISO 11357-3

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D, molded	65		ISO 868
Tensile modulus
2 mm, molded into shape	1450	MPa	ISO 527-2/1BA/50
tensile strength			ISO 527-2/1BA/50
Yield, 2 mm, molded	32.0	MPa	ISO 527-2/1BA/50
Fracture, 2 mm, molded	15.0	MPa	ISO 527-2/1BA/50
Tensile strain
Fracture, 2 mm, molded	> 200	%	ISO 527-2/1BA/50
Bending modulus
2 mm, molded into shape	1700	MPa	ISO 178
bending strength
2 mm, molded into shape	32.0	MPa	ISO 178

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.