| About |
|---|
| P6006 is black compound high density (class MRS 10 – PE 100) Polyethylene with bimodal distribution of molecular mass. It is specifically designed for Pressure Pipe applications. It provides excellent stress crack resistance properties (ESCR) combined with very good long term hydrostatic strength. Pressure pipes for drinking water, irrigation, gas distribution and waste water pipes. It is also recommended for manufacture of chemical liners and containers.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Food contact compliance,Bimodal molecular weight distribution,High ESCR |
| Availabilitys | North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.959 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，21.6kg | 6.2 | g/10min | ISO 1133 |
| 190℃，5.0kg | 0.23 | g/10min | ISO 1133 |
| Carbon black content | 2.3 | % | ISO 6964 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 13 | kJ/m² | ISO 179 |
| 23℃ | 26 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 74.0 | ℃ | ISO 306 |
| Oxygen sensing time | |||
| 210℃ | > 20 | min | EN 728 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 63 | ISO 868 | |
| Tensile modulus | |||
| 2 mm, molded into shape | 900 | MPa | ISO 527-2/1BA/50 |
| tensile strength | |||
| Yield, 2 mm, molded | 23.0 | MPa | ISO 527-2/1BA/50 |
| Tensile strain | |||
| Yield, 2 mm, molded | 9.0 | % | ISO 527-2/1BA/50 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 190 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |