SABIC® HDPE PCG453

About
SABIC® HDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® HDPE PCG453 is typically used for the injection moulding of healthcare packaging, caps and closures and other parts for medical packaging. This grade has a very high impact resistance, even at low temperatures. Compliance to regulations. SABIC® HDPE PCG453 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI).&&

About

SABIC® HDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® HDPE PCG453 is typically used for the injection moulding of healthcare packaging, caps and closures and other parts for medical packaging. This grade has a very high impact resistance, even at low temperatures. Compliance to regulations. SABIC® HDPE PCG453 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI).&&

Product Description
Supplier	SABIC
Generic	HDPE
Material Status	Commercial: Active
Features	High purity,High impact resistance,High density,low-temperature impact resistance
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.953	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	4.7	g/10min	ISO 1133
190℃，5.0kg	13	g/10min	ISO 1133

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	81	℃	ISO 75-2/Bf
Melting temperature	132	℃	ISO 11357-3
Vicat Softening Temp
B50	124	℃	ISO 306

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	4	kJ/m²	ISO 180-1A

MECHANICAL	Nominal value	Unit	Test method
Shaw’s D-molding	61		ISO 868
tensile strength
23℃	26	MPa	ISO 527-2
Tensile strain
Fracture, 23 ℃	>200	%	ISO 527-2
Tensile modulus
23℃	1100	MPa	ISO 527-2
bending strength
23℃	26	MPa	ISO 178
Bending modulus
23℃	1200	MPa	ISO 178

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.