| SABIC® HDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® HDPE PCG80063 is designed for the injection moulding of healthcare packaging, caps and closures and other parts for medical packaging. It is an easy-to-process, stiff grade. SABIC® HDPE PCG80063 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). The product mentioned herein may not be used for medical healthcare devices or materials intended for temporary or permanent implementation in the human body.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,High purity |
| Availabilitys | North America,Latin America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.963 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，2.16kg | 8.0 | g/10min | ISO 1133 |
| 190℃，5.0kg | 23 | g/10min | ISO 1133 |
| Melt Volume Rate | ISO 1133 | ||
| 190℃，2.16 kg | 11.0 | cm³/10min | ISO 1133 |
| 190℃，5 kg | 30.0 | cm³/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 60 ℃, 3.00 mm, detergent | 40.0 | hr | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ISO 180/A | ||
| -30 ℃, molded | 4.0 | kJ/m² | ISO 180-A |
| 23 ℃, molded | 4.0 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 94.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 129 | ℃ | ISO 306/A |
| Melting temperature | |||
| DSC | 134 | ℃ | DIN 53765 |
| Enthalpy Change | 226 | J/g | DIN 53765 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 65 | ISO 868 | |
| Tensile modulus | |||
| 2 mm, molded into shape | 1450 | MPa | ISO 527-2/1BA/50 |
| tensile strength | ISO 527-2/1BA/50 | ||
| Yield, 2 mm, molded | 31.0 | MPa | ISO 527-2/1BA/50 |
| Fracture, 2 mm, molded | 15.0 | MPa | ISO 527-2/1BA/50 |
| Tensile strain | |||
| Fracture, 2 mm, molded | > 200 | % | ISO 527-2/1BA/50 |
| Tensile creep modulus | ISO 899-1 | ||
| 1 hr | 625 | MPa | ISO 899-1 |
| 1000 hr | 275 | MPa | ISO 899-1 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2 MPa |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |