| SABIC® HDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® HDPE PCGF0863 resin is a high density homopolymer with good barrier properties. The grade offers high stiffness, high temperature resistance and relatively high grease resistance. The resin has a low gel level. Application SABIC® HDPE PCGF0863 is typically used for flexible packaging, pharmaceuticals and devices and release liners. Compliance to regulations SABIC® HDPE PCGF0863 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI).&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High purity,Low speed solidification point,High Heat Resistance,Inoxidizability,Grease resistance,High density,Block resin,Homopolymer |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.964 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 8.0 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Tensile modulus | ISO 527-3 | ||
| MD, 25 µ m, cast thin film | 580 | MPa | ISO 527-3 |
| TD, 25 µ m, cast thin film | 580 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, yield, 25 µ m, blow molded film | 26.0 | MPa | ISO 527-3 |
| TD, yield, 25 µ m, blow molded film | 24.0 | MPa | ISO 527-3 |
| MD, fracture, 25 µ m, blow molded film | 22.0 | MPa | ISO 527-3 |
| TD, fracture, 25 µ m, blow molded film | 18.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 25 µ m, cast thin film | 700 | % | ISO 527-3 |
| TD, fracture, 25 µ m, cast thin film | 800 | % | ISO 527-3 |
| Oxygen permeability | |||
| 23 ℃, 25 µ m, cast thin film | 0.100 | cm³/m²/24 hr | Internal Method |
| Water vapor transmittance | |||
| 38 ℃, 100% RH, 25 µ m, cast thin film | 4.0 | g/m²/24 hr | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| DSC | 134 | ℃ | DIN 53765 |
| Enthalpy Change | 224 | J/g | DIN 53765 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0% RH |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |