SABIC® LDPE 2008N0

About
SABIC® LDPE 2008N0 is a LDPE tubular grade without additives. SABIC® LDPE 2008TN00 is produced using SABIC Clean Tubular Reactor (CTR) Technology which ensure grades with high purity. It exhibits high toughness with good flexibility and reasonable environmental stress cracking resistance and is therefore typically used for flexibles and tough articles. Application SABIC® LDPE 2008N0 is typically suitable for injection moulding application, frequently used for caps & closures. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

About

SABIC® LDPE 2008N0 is a LDPE tubular grade without additives. SABIC® LDPE 2008TN00 is produced using SABIC Clean Tubular Reactor (CTR) Technology which ensure grades with high purity. It exhibits high toughness with good flexibility and reasonable environmental stress cracking resistance and is therefore typically used for flexibles and tough articles. Application SABIC® LDPE 2008N0 is typically suitable for injection moulding application, frequently used for caps & closures. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

Product Description
Supplier	SABIC
Generic	LDPE
Material Status	Commercial: Active
Features	Good flexibility,High purity,Low density,High ESCR
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.920	g/cm³	ISO 1183
Melt Flow Rate			ISO 1133
190℃，2.16kg	7.5	g/10min
190℃，5.0kg	28	g/10min
Melt Volume Rate			ISO 1133
190℃，2.16 kg	10.0	cm³/10min
190℃，5 kg	33.0	cm³/10min

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch			ISO 180/A
-30 ℃, injection molding	9.0	kJ/m²
23 ℃, injection molding	45	kJ/m²

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	43.0	℃	ISO 75-2/B
Vicat Softening Temp	89.0	℃	ISO 306/A
Melting temperature
DSC	107	℃	DIN 53765
Enthalpy Change	125	J/g	DIN 53765

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D, injection molding	40		ISO 868
Tensile modulus
injection molding	130	MPa	ISO 527-2/50
tensile strength			ISO 527-2/50
Yield, injection molding	8.00	MPa
Fracture, injection molding	10.0	MPa
Tensile strain
Fracture, injection molding	120	%	ISO 527-2/50

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.