| About |
|---|
| SABIC® LDPE 2200H2 is a grade with a low melt flow rate and contains a low level of anti block and a medium level of slip agent (E=erucamide). This grade shows a good draw down ability and good optical properties. Application SABIC® LDPE 2200TC12 is typically used for thin film applications requiring high strength and thin shrink film with high shrink forces and wrapping strength. Typical applications are lamination and coextruded films. This product is not intended for and must not be used in any pharmaceutical/medical applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low liquidity,Good dissection,Optical performance,Low density,Low anti-blocking |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.922 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.33 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Blown film | 0.20 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| Tensile modulus | ISO 527-3 | ||
| MD, 50 µ m, blow molded film | 190 | MPa | |
| TD, 50 µ m, blow molded film | 190 | MPa | |
| tensile strength | ISO 527-3 | ||
| MD, yield, 50 µ m, blow molded film | 11.0 | MPa | |
| TD, yield, 50 µ m, blow molded film | 11.0 | MPa | |
| MD, fracture, 50 µ m, blow molded film | 27.0 | MPa | |
| TD, fracture, 50 µ m, blow molded film | 22.0 | MPa | |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 50 µ m, blow molded film | > 200 | % | |
| TD, fracture, 50 µ m, blow molded film | > 500 | % |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod notched impact strength | |||
| 50 µ m, blow molded | 300 | J/cm | ASTM D4272 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 50.0 µ m, blow molded film | 57 | ASTM D2457 | |
| Haze | |||
| 50 µ m, blow molded film | 9.0 | % | ASTM D1003A |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Blocking force | |||
| Blow molded film, 50.0 µ m | 20 | g | Internal Method |
| Re blocking – blow molded film (50.0 µ m) | g | Internal Method | |
| tear strength | ISO 6383-2 | ||
| MD，50 µm | 35.0 | kN/m | |
| TD，50 µm | 40.0 | kN/m | |
| memo_intro |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Blown Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |