| About |
|---|
| PRODUCT DESCRIPTION: SABlC® LDPE HP2027L is a Low Density Polyethylene grade formulated with slip agent, with increased density. It typically exhibits better draw down ability with high output. Films typically have excellent optics with low friction and high rigidity. TYPICAL APPLICATIONS: Thin shrink film, lamination film, packaging films for food and industrial goods, bags & pouches. This grade is typically suitable where high optics, enhanced stiffness and down gauging are required. This product is not intended for use in medical and pharmaceutical applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Smoothness,Good dissection,Optical performance,Low coefficient of friction,Food contact compliance,Low density |
| Availabilitys | North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.927 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 0.05 mm | 300 | MPa | ISO 527-2 |
| friction coefficient | < 20 | % | ISO 8295 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| film thickness | 20 – 60 micron | ||
| tensile strength | ISO 527-3 | ||
| Yield, 0.05 mm | 13.0 | MPa | ISO 527-2 |
| MD, fracture, 50 µ m, blow molded film | 25.0 | MPa | ISO 527-3 |
| TD, fracture, 50 µ m, blow molded film | 18.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 50 µ m, blow molded film | 350 | % | ISO 527-3 |
| TD, fracture, 50 µ m, blow molded film | 600 | % | ISO 527-3 |
| Drop hammer impact | |||
| 50 µ m, blow molded film | 110 | g | ASTM D1709 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| A50 | 100 | ℃ | ISO 306/A50 |
| Melting temperature | |||
| DSC | 114 | ℃ | ISO 3146 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | ASTM D2457 | ||
| 20 °, 50 µ m, blow molded film | > 70 | ASTM D2457 | |
| 60 °, 50.0 µ m, blow molded film | > 110 | ASTM D2457 | |
| Haze | |||
| 50 µ m, blow molded film | < 7.0 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Blow（up Ratio） | 2.00 to 3.00 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 160 to 200 | °C | |
| Notes |
|---|
| 1. Erucamide |
| 2. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |