| Product Description 120W is a Linear Low Density Polyethylene grade featuring superior clarity for flexible packaging. Film exhibits excellent optical properties with good tensile and impact strength properties. Formulation: 1500 ppm Slip & 3000 ppm Antiblock Typical Applications High clarity applications, paper overwrap, produce and bread bags, garment and liners&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good flexibility,High impact resistance,Smoothness,High anti-blocking,Good Tensile Strength,Copolymer |
| Availabilitys | North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 30 | µm | |
| Secant modulus | ASTM D882 | ||
| MD：30 µm | 260 | MPa | ASTM D882 |
| TD：30 µm | 270 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 30 µ m | 10.0 | MPa | ASTM D882 |
| TD, yield, 30 µ m | 9.00 | MPa | ASTM D882 |
| MD, fracture, 30 µ m | 38.0 | MPa | ASTM D882 |
| TD, fracture, 30 µ m | 30.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 30 µ m | 650 | % | ASTM D882 |
| TD, fracture, 30 µ m | 810 | % | ASTM D882 |
| Drop hammer impact | |||
| 30 µm | 120 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：30 µm | 160 | g | ASTM D1922 |
| TD：30 µm | 350 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 100 | ℃ | ASTM D1525 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60°，30.0 µm | 90 | ASTM D2457 | |
| Haze | |||
| 30 µm | 10 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Puncture resistance | |||
| 30.0 µm | 600 | J/cm | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 195 to 215 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |