| About |
|---|
| 120WJ is a Linear Low Density Polyethylene TNPP free grade suitable for general purpose packaging. Films produced using these resins gives good tensile properties, impact strength and excellent optical properties. 120WJ contains slip and antiblock additive. |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Smoothness,High anti-blocking |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | |||
| 1% secant, MD | 260 | MPa | |
| 1% secant, TD | 270 | MPa | |
| Tensile strength | |||
| MD: Yield | 10.0 | MPa | |
| TD: Yield | 9.00 | MPa | |
| MD: Fracture | 38.0 | MPa | |
| TD: Fracture | 30.0 | MPa | |
| Tensile strain | |||
| MD, fracture | 650 | % | |
| TD, fracture | 810 | % | |
| Elmandorf tear strength | |||
| MD | 160 | g | |
| TD | 350 | g |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 100 | ℃ | ASTM D1525 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | 90 | ASTM D2457 | |
| Haze | |||
| 30.0 µ m, blow molded film | 10 | % | ASTM D1003 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |