SABIC® LLDPE 218BE (Film)

About
SABIC® LLDPE 218BE is a butene linear low density polyethylene resin with an additive package typically designed for a broader range of food applications (TNPP free). The good thermal stability allows to use the resin in critical extrusion processing conditions. Films produced from SABIC® LLDPE 218BE have better draw-down ability compared to lower MFR LLDPE resins. SABIC® LLDPE 218BE is a Linear Low Density Polyethylene natural resin typically used for wire and cable applications. SABIC® LLDPE 218BE contains a high level of antioxidants and does not contain any antiblock and/or slip agents. It also exhibits good Environmental Stress Crack Resistance (ESCR). Sufficient Cu-inhibitor should be added to meet specific ageing requirements. For jacketing applications, addition of Carbon Black or UV stabilizer is required. Application Blown Film: SABIC® LLDPE 218BE is typically used for food applications (lamination film, barrier film) but can also be used in industrial packaging and as blending partner with other SABIC® PE resins in both blown and cast film applications. Cast Film: SABIC® LLDPE 218BE is typically used for food applications (lamination film, barrier film) and pallet hand wrap. Masterbatch Compounding: It is suitable for additive masterbatches (eg. slip agents, anti fog agents, anti static agents, thermal stabilizers) in film and blow moulding applications. Wire & Cable Extrusion: Telecommunication and Power cable (LV, MV, HV) jacketing. Halogen-free flame retardant (HFFR) compounds. One-step or two-steps silane crosslinkable for cable insulation. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications.&&

About

SABIC® LLDPE 218BE is a butene linear low density polyethylene resin with an additive package typically designed for a broader range of food applications (TNPP free). The good thermal stability allows to use the resin in critical extrusion processing conditions. Films produced from SABIC® LLDPE 218BE have better draw-down ability compared to lower MFR LLDPE resins. SABIC® LLDPE 218BE is a Linear Low Density Polyethylene natural resin typically used for wire and cable applications. SABIC® LLDPE 218BE contains a high level of antioxidants and does not contain any antiblock and/or slip agents. It also exhibits good Environmental Stress Crack Resistance (ESCR). Sufficient Cu-inhibitor should be added to meet specific ageing requirements. For jacketing applications, addition of Carbon Black or UV stabilizer is required. Application Blown Film: SABIC® LLDPE 218BE is typically used for food applications (lamination film, barrier film) but can also be used in industrial packaging and as blending partner with other SABIC® PE resins in both blown and cast film applications. Cast Film: SABIC® LLDPE 218BE is typically used for food applications (lamination film, barrier film) and pallet hand wrap. Masterbatch Compounding: It is suitable for additive masterbatches (eg. slip agents, anti fog agents, anti static agents, thermal stabilizers) in film and blow moulding applications. Wire & Cable Extrusion: Telecommunication and Power cable (LV, MV, HV) jacketing. Halogen-free flame retardant (HFFR) compounds. One-step or two-steps silane crosslinkable for cable insulation. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications.&&

Product Description
Supplier	SABIC
Generic	Linear low density polyethylene
Material Status	Commercial: Active
Features	Food contact compliance,Inoxidizability,Low density,Butylene copolymer,Heat Stabilized
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.918	g/cm³	ISO 1183/A
Melt Flow Rate
190℃，2.16kg	2.1	g/10min	ISO 1133

film	Nominal value	Unit	Test method
film thickness
test	20	µm
Elastic Recovery (cast film, 20.0 µ m)	53	%	ASTM D5459
Corrosion Function Resistance – Cast thin film (20.0 µ m)	2.20	J	ASTM D5748
Retention Force（60 sec，20.0 µm）	970	g
Stress Retention (cast film, 20.0 µ m)	80	%	ASTM D5459
Ultimate Pre-stretch Level – Cast Film (20.0 µm)	310	%

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	96.0	℃	ISO 306/A
Melting temperature
DSC	122	℃	Internal Method

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	5.0E+15	ohms·cm	ASTM D257
Dielectric strength	55	kV/mm	ASTM D149
Dielectric constant
60 Hz	2.17		ASTM D150
Dissipation factor
60 Hz	1.0E-3		ASTM D150

optical performance	Nominal value	Unit	Test method
gloss
45 °, 20 µ m, cast thin film	92		ASTM D2457
Haze
20.0 µ m, cast thin film	1.2	%	ASTM D1003A

Supplementary information	Nominal value	Unit	Test method
Drop hammer impact
20.0 µ m, cast thin film	28.0	J/cm	ISO 7765-2
Peel Cling			ASTM D5458
0% pre-stretch：20.0 µm	153.0	g/2.5 cm	ASTM D5458
200% pre-stretch：20.0 µm	127.5	g/2.5 cm	ASTM D5458
tear strength
TD，20 µm	185.0	kN/m	ISO 6383-2

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	48		ASTM D2240
tensile strength			ASTM D638
yield	12.0	MPa	ASTM D638
fracture	17.0	MPa	ASTM D638
Tensile strain			ASTM D638
yield	16	%	ASTM D638
fracture	790	%	ASTM D638
Bending modulus
1% secant	254	MPa	ASTM D790

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	250 to 300	°C

Notes
1. Typical properties: these are not to be construed as specifications.
2. Cast Film
3. 500 V/sec
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.