SABIC® LLDPE 6135BE

About
SABIC® LLDPE 6135BE is a medium density grade typically used in high demanding extrusion segments like e.g. sheet and more specific geo-membranes. The grade is a hexene-1 copolymer combining good extrusion performance, mechanical properties and ESCR with low migration figures because of the increased density compared to LLDPE grades. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

About

SABIC® LLDPE 6135BE is a medium density grade typically used in high demanding extrusion segments like e.g. sheet and more specific geo-membranes. The grade is a hexene-1 copolymer combining good extrusion performance, mechanical properties and ESCR with low migration figures because of the increased density compared to LLDPE grades. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

Product Description
Supplier	SABIC
Generic	Linear low density polyethylene
Material Status	Commercial: Active
Features	Copolymer,Low to no mobility,Hexene copolymers,High ESCR
Availabilitys	Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.932	g/cm³	ISO 1183
Melt Flow Rate			ISO 1133
190℃，2.16kg	0.80	g/10min	ISO 1133
190℃，5.0kg	2.4	g/10min	ISO 1133

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179/1eA
-30 ℃, molded	9.0	kJ/m²	ISO 179/1eA
23 ℃, molded	30	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	60.0	℃	ISO 306/B
Melting temperature
DSC	118 to 122	℃	DIN 53765
Oxygen sensing time
Compression molding, 210 ℃, 1.60 mm	> 50	min	EN 728

Supplementary information	Nominal value	Unit	Test method
Notched Constant Tensile Load (molded, 1.60 mm)	> 2.7	month	ASTM D5397

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D, molded	54		ISO 868
Tensile modulus
1.60 mm, molded	620	MPa	ISO 527-2/200
tensile strength
Yield, 1.60 mm, molded	18.0	MPa	ISO 527-2/200
Tensile strain			ISO 527-2/200
Yield, 1.60 mm, molded	12	%	ISO 527-2/200
Fracture, 1.60 mm, molded	> 700	%	ISO 527-2/200

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.