| About |
|---|
| SABIC® LLDPE 726N is a butene linear low density polyethylene resin. This grade is typically designed to give blown films a relatively high stiffness for good machinability and a good overall balance of other performance properties, such as puncture resistance, impact strength and heat sealability. Application Typical applications for SABIC® LLDPE 726N are shipping sacks, produce bags, can liners and carrier bags. SABIC® LLDPE 726N has good optical properties when blended with a LDPE (15-85%). This product is not intended for and must not be used in any pharmaceutical/medical applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good heat sealing,High impact resistance,Machinable,Inoxidizability,Low density,Butylene copolymer,Puncture Resistant |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.925 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.70 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| Tensile modulus | ISO 527-3 | ||
| MD, 50 µ m, blow molded film | 220 | MPa | ISO 527-3 |
| TD, 50 µ m, blow molded film | 240 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, yield, 50 µ m, blow molded film | 13.0 | MPa | ISO 527-3 |
| TD, yield, 50 µ m, blow molded film | 14.0 | MPa | ISO 527-3 |
| MD, fracture, 50 µ m, blow molded film | 45.0 | MPa | ISO 527-3 |
| TD, fracture, 50 µ m, blow molded film | 35.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 50 µ m, blow molded film | 650 | % | ISO 527-3 |
| TD, fracture, 50 µ m, blow molded film | 850 | % | ISO 527-3 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod notched impact strength | |||
| 50 µ m, blow molded | 160 | J/cm | ASTM D4272 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 110 | ℃ | ISO 306/A |
| Melting temperature | |||
| DSC | 124 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 50.0 µ m, blow molded film | 60 | ASTM D2457 | |
| Haze | |||
| 50 µ m, blow molded film | 12 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Puncture resistance | |||
| Blow molded film, 50.0 µ m | 650 | J/m | Internal Method |
| tear strength | ISO 6383-2 | ||
| MD，50 µm | 20.0 | kN/m | ISO 6383-2 |
| TD，50 µm | 130.0 | kN/m | ISO 6383-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Blown Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |