| SABIC® LLDPE M500026 SABIC® LLDPE M500026 is a high flow, linear low density polyethylene copolymer injection moulding grade with a narrow molecular weight distribution. It has been typically designed to have good low temperature toughness, stress crack resistance (ESCR), mouldability and gloss. Typical applications. Injection Molding: SABIC® LLDPE M500026 is typically used for injection moulding of containers, reclosure lids and fast cycle, deep draw injection moulding applications, which takes advantage of its high flow properties. Also, the higher melting point of the material allows for high end-use temperature when compared with conventional polyethylenes of equal density. Masterbatch Compounding: SABIC® LLDPE M500026 resin is typically used for injection moulding masterbatch where a high filler acceptance is required combined with a good flow. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&SABIC® LLDPE M500026 Product Description M500026 is Linear Low Density Polyethylene grade with narrow molecular weight distribution suitable for injection molding applications. It has been designed to give excellent flow properties with better low temperature toughness, stress crack resistance and gloss. Typical Applications M500026 is recommended for lids for closures and containers and deep draw houseware products, automotive parts etc.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good surface appearance,High liquidity,Quick molding cycle,Weight distribution,Low density,Copolymer,Low temperature toughness,High ESCR |
| Availabilitys | North America,Latin America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.926 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 50 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 100% non-ionic detergent, molded, F50 | 2.00 | hr | ASTM D1693A |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, molded | 450 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -75.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 88.0 | ℃ | ASTM D1525 1 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 55 | ASTM D2240 | |
| Tensile modulus | |||
| 1% cut, molded | 354 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| Yield, molding | 13.0 | MPa | |
| Fracture, molded | 12.4 | MPa | |
| Tensile strain | |||
| Fracture, molded | 120 | % | ASTM D638 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 180 to 230 | °C | |
| Mold temperature | 5.00 to 30.0 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |