| About |
|---|
| SABIC® LLDPE MG200024 SABIC® LLDPE MG200024 is a high flow linear low density polyethylene copolymer grade with a narrow molecular weight distribution. SABIC® LLDPE MG200024 is in powder form. Application SABIC® LLDPE MG200024 is typically used for masterbatches with very high carbon black, titanium dioxide or pigment content in blow moulding, injection moulding and film extrusion applications. Since the resin is supplied in free flowing powder form, it can be used for masterbatch production where PE powders are used. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&SABIC® LLDPE MG200024 SABIC® LLDPE MG200024 is a high flow linear low density polyethylene copolymer grade with a narrow molecular weight distribution. SABIC® LLDPE MG 200024 is in powder form. SABIC® LLDPE MG200024 is well suited for masterbatch applications like blow moulding, injection moulding and film extrusion. Especially for masterbatches with very high carbon black, titanium dioxide or pigment content. Since the resin is supplied in powder form, it is extremely suited for masterbatch production where PE powders are used. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | High liquidity,Weight distribution,Low density,Copolymer |
| Availabilitys | North America,Latin America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 20 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| Compression Molding | 24.0 | hr | ASTM D1693 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, molded | 540 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -75.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 94.0 | ℃ | ASTM D1525 1 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 55 | ASTM D2240 | |
| Tensile modulus | |||
| 1% cut, molded | 315 | MPa | ASTM D638 |
| tensile strength | ASTM D638 | ||
| Yield, molding | 12.0 | MPa | |
| Fracture, molded | 8.50 | MPa | |
| Tensile strain | |||
| Fracture, molded | 450 | % | ASTM D638 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 190 to 230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 3. Rate A (50°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |