| About |
|---|
| SABIC® SUPEER™ 8118 is an ethylene-octene copolymer produced via Nexlene™ Technology. It performs well in a wide range of general purpose and high performance LLDPE blown film applications and has good processablity. Application Typical applications for SABIC® SUPEER™ 8118 are lamination film, frozen bags, liquid pouches, heavy duty bags, industrial liner, agriculture film, stretch hood, surface protective film. This product is not intended for and must not be used in any pharmaceutical/medical applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | mLLDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Low density,Octene copolymer,Copolymer |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.1 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| Secant modulus | ASTM D882 | ||
| 1% secant, MD: 50 µ m, blow molded film | 140 | MPa | ASTM D882 |
| 1% secant, TD: 50 µ m, blow molded film | 156 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 50 µ m, blow molded film | 12.0 | MPa | ASTM D882 |
| TD, yield, 50 µ m, blow molded film | 11.0 | MPa | ASTM D882 |
| MD, fracture, 50 µ m, blow molded film | 54.0 | MPa | ASTM D882 |
| TD, fracture, 50 µ m, blow molded film | 54.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 50 µ m, blow molded film | 630 | % | ASTM D882 |
| TD, fracture, 50 µ m, blow molded film | 730 | % | ASTM D882 |
| Drop hammer impact | |||
| 50 µ m, blow molded film | 1000 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD: 50 µ m, blow molded film | 14 | g | ASTM D1922 |
| TD: 50 µ m, blow molded film | 22 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 115 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 50 µ m, blow molded film | 10 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Blown Film Melt Temperature | 180 to 200 | ℃ | |
| Blow（up Ratio） | 2.00 to 3.00 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. F50 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |