SABIC® mLLDPE 8318

About
SABIC® mLLDPE 8318 is an ethylene-octene copolymer produced via Nexlene™ Technology. It performs well in a wide range of high performance LLDPE cast film applications and has good impact strength and transparency. SABIC® mLLDPE 8318 does not contain slip and anti-block agent. Application Typical applications for SABIC® mLLDPE 8318 are stretch wrap film, silage film and breathable film. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

About

SABIC® mLLDPE 8318 is an ethylene-octene copolymer produced via Nexlene™ Technology. It performs well in a wide range of high performance LLDPE cast film applications and has good impact strength and transparency. SABIC® mLLDPE 8318 does not contain slip and anti-block agent. Application Typical applications for SABIC® mLLDPE 8318 are stretch wrap film, silage film and breathable film. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

Product Description
Supplier	SABIC
Generic	mLLDPE
Material Status	Commercial: Active
Features	High impact resistance,Low density,Octene copolymer,Copolymer
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.918	g/cm³	ASTM D1505
Melt Flow Rate
190℃，2.16kg	3.0	g/10min	ASTM D1238

film	Nominal value	Unit	Test method
film thickness
test	40	µm
tensile strength			ASTM D882
MD, yield, 40 µ m, blow molded film	9.80	MPa	ASTM D882
TD, yield, 40 µ m, blow molded film	9.50	MPa	ASTM D882
MD, fracture, 40 µ m, blow molded film	49.0	MPa	ASTM D882
TD, fracture, 40 µ m, blow molded film	54.0	MPa	ASTM D882
Tensile strain			ASTM D882
MD, fracture, 40 µ m, extruded film	600	%	ASTM D882
TD, fracture, 40 µ m, extruded film	650	%	ASTM D882
Drop hammer impact
40 µ m, cast thin film	400	g	ASTM D1709
Elmandorf tear strength			ASTM D1922
MD: 40 µ m, cast thin film	10	g	ASTM D1922
TD: 40 µ m, cast thin film	23	g	ASTM D1922

THERMAL	Nominal value	Unit	Test method
Melting temperature	115	℃	Internal Method

optical performance	Nominal value	Unit	Test method
Haze
40 µ m, cast thin film	2.0	%	ASTM D1003

Supplementary information	Nominal value	Unit	Test method
	250 to 300	℃

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.