| About |
|---|
| PC1000R resin is a medium-low flow (MFR = 10 at 300°C/1.2kg), heat stabilized, polycarbonate product with mold release designed for use in the general purpose molding market. It is available exclusively at www.sabicpc.com&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Moderate liquidity,Heat Stabilized,V-2 |
| Availabilitys | North America,Europe,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 10 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 9.50 | cm³/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| On the stretching rod | 0.50 to 0.70 | % | |
| MD：3.2 mm | 0.50 to 0.70 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.35 | % | ISO 62 |
| Equilibrium, 23 ℃ | 0.35 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 800 | J/m | ASTM D256 |
| -30℃，80*10*3 | 12 | kJ/m² | ISO 180-1A |
| 23℃，80*10*3 | 70 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 无断裂 | ASTM D4812, ISO 180/1U | |
| -30℃，80*10*4 | 无断裂 | ISO 180/1U | |
| Dart impact equipped with measuring instruments | |||
| 23 ℃, peak energy load | 65.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 138 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 138 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.2 mm | 127 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64.0 mm span standard B (120 ℃/h), load 2 (50N) | 127 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B50 | 143 | ℃ | ISO 306/B50, ASTM D1525 15 |
| Ball pressure test | |||
| 125℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD | |||
| Thermal conductivity coefficient | 0.20 | W/m/K | ASTM C177, ISO 8302 |
| -40 to 95 ℃ | 7.0E-5 | cm/cm/℃ | ASTM E831 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| 23 to 80 ℃ | 7.0E-5 | cm/cm/℃ | ISO 11359-2 |
| Volume resistivity | > 1.0E+15 | ohms·cm | ASTM D257，IEC 60093 |
| Dielectric strength | |||
| 1.6 mm | 27 | kV/mm | ASTM D149，IEC 60243-1 |
| Dielectric constant | ASTM D150, IEC 60250 | ||
| 60 Hz | 3.00 | ||
| 1 MHz | 3.00 | ||
| Dissipation factor | ASTM D150, IEC 60250 | ||
| 60 Hz | 1.0E-3 | ||
| 1 MHz | 0.010 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-2 | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.586 | ASTM D542，ISO 489 | |
| Transmittance | |||
| 2540 µm | 88.0 to 90.0 | % | ASTM D1003 |
| Haze | |||
| 2540 µm | < 0.80 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 120 | ASTM D785 | |
| R-level | 120 | ISO 2039-2 | |
| Tensile modulus | |||
| 50 mm/min | 2350 | MPa | ASTM D638 |
| 2350 | MPa | ISO 527-1-2 | |
| tensile strength | |||
| Yield, Type I, 50 mm/min | 63.0 | MPa | ASTM D638 |
| yield | 63.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Yield, Type I, 50 mm/min | 6.0 | % | ASTM D638 |
| yield | 6.0 | % | ISO 527-2/50 |
| Fracture, Type I, 50 mm/min | > 70 | % | ASTM D638 |
| fracture | > 70 | % | ISO 527-2/50 |
| Bending modulus | |||
| 50.0 mm 跨距 1.3 mm/min | 2300 | MPa | ASTM D790 |
| 2 mm/min | 2300 | MPa | ISO 178 |
| bending strength | |||
| 1.30 mm/min | 90.0 | MPa | ISO 178 |
| Yield, 50 mm span 80 * 10 * 3 | 90.0 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 60.0 to 80.0 | °C | |
| Barrel rear temperature | 260 to 280 | °C | |
| Barrel middle temperature | 270 to 290 | °C | |
| Barrel front temperature | 280 to 310 | °C | |
| Nozzle temperature | 270 to 290 | °C | |
| Processing (melt) temperature | 280 to 310 | °C | |
| Mold temperature | 80.0 to 110 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 2.0 in/min |
| 4. Type I, 2.0 in/min |
| 5. 0.051 in/min |
| 6. 0.079 in/min |
| 7. Yield |
| 8. 80*10*3 |
| 9. 80*10*4 mm |
| 10. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |