| About |
|---|
| PC5800 resin is a very high flow (MFR = 8.9 at 250C/1.2kg) polycarbonate product designed for use in the optical media market. It is available exclusively at www.sabicpc.com.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | High liquidity |
| Availabilitys | Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Flow Rate | |||
| 250℃，1.2 kg | 8.9 | g/10min | ASTM D1238 |
| 300℃，1.2 kg | 58 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 250℃，1.2 kg | 8.0 | cm³/10min | ISO 1133 |
| Molding shrinkage | |||
| MD | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | |||
| Saturation, 23 ℃ | 0.35 | % | ISO 62 |
| Equilibrium, 23 ℃ | 0.35 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Modulus | |||
| 50 mm/m | 2350 | MPa | ASTM D638 |
| 1 mm/min | 2350 | MPa | ISO 527-1-2 |
| Tensile Strength | |||
| yield | 60.0 | MPa | ASTM D638 |
| yield | 60.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| yield | 6.0 | % | ASTM D638 |
| yield | 6.0 | % | ISO 527-2/50 |
| fracture | > 40 | % | ASTM D638 |
| fracture | > 40 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50 mm span | 2300 | MPa | ASTM D790 |
| — | 2300 | MPa | ISO 178 |
| Flexural Strength | |||
| — | 90.0 | MPa | ISO 178 |
| Yield, 50 mm span | 90.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact strength | ISO 180/1A | ||
| -30℃ | 12 | kJ/m² | |
| 23℃ | 15 | kJ/m² | |
| Izod Unnotched Impact strength of cantilever beam | ISO 180/1U | ||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 0.45 MPa, unannealed, 3.2 mm | 132 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 132 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.2 mm | 122 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 122 | ℃ | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| B50 | 138 | ℃ | ISO 306/B50, ASTM D1525 14 |
| Ball Pressure Test | |||
| 125℃ | Pass | IEC 60695-10-2 | |
| Coeff. of linear thermal expansion | |||
| MD | |||
| -40 to 95 ℃ | 7.0E-5 | cm/cm/℃ | ASTM E831 |
| 23 to 80 ℃ | 7.0E-5 | cm/cm/℃ | ISO 11359-2 |
| Thermal conductivity | 0.20 | W/m/K | ASTM C177, ISO 8302 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistance | > 1.0E+15 | ohms·cm | IEC 60093 |
| Relative permittivity | |||
| 1 MHz | 3.00 | IEC 60250 | |
| Dissipation Factor | |||
| 1 MHz | 0.010 | IEC 60250 |
| OPTICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542，ISO 489 | |
| Light Transmission | |||
| 2540 µm | > 90.0 | % | ASTM D1003 |
| Haze | |||
| 2540 µm | < 0.70 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Maximum Moisture Content | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature Zone 1 | 270 to 290 | °C | |
| Middle Temperature Zone 2 | 320 to 340 | °C | |
| Front Temperature Zone 3 | 350 to 380 | °C | |
| Nozzle temperature | 340 to 370 | °C | |
| Melt Temperature | 340 to 370 | °C | |
| Mold Temperature | 75.0 to 95.0 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 2.0 in/min |
| 4. Type I, 2.0 in/min |
| 5. 0.051 in/min |
| 6. 0.079 in/min |
| 7. Yield |
| 8. 80*10*3 |
| 9. 80*10*4 mm |
| 10. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |