| SABIC® PP 108MF10 is a super high impact copolymer which exhibits an unmatched cold impact resistance, high flow and excellent paint adhesion characteristics. Because of this unique and well balanced property profile our customers commonly use this material for painted car bumpers. SABIC® PP 108MF10 is a designated automotive grade.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | High impact resistance,High liquidity,Sprayable,Nucleation,low-temperature impact resistance,Impact copolymer |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：24 hrs | 1.5 | % | ISO 294-4 |
| TD：24 hrs | 1.5 | % | ISO 294-4 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| A50 | 130 | ℃ | ISO 306/A50 |
| B50 | 50 | ℃ | ISO 306 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 52 | ISO 868 | |
| tensile strength | |||
| 23℃ | 19 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 8.0 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 1000 | MPa | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | NB | kJ/m² | ISO 180-1A |
| Charpy Unnotch Impact strength | |||
| 23℃ | NB | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | NB | kJ/m² | ISO 179/1eA |
| Notched impact strength of cantilever beam | |||
| 23℃ | NB | kJ/m² | ISO 180/1U |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. 2.0 in/min |
| 4. Rate B (120°C/h), Loading 1 (10 N) |
| 5. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |